Electroluminescence from Nanocrystals above 2 µm

Abstract : Visible nanocrystal-based light-emitting diodes (LEDs) are about to become commercially available. However, their infrared counterparts suffer from two key limitations. First, III–V semiconductor technologies are strong competitors. Second, their potential for operation beyond 1.7 µm remains unexplored. The range from 1.5 to 4 µm corresponds to a technological gap in which the efficiency of interband quantum-well-based devices vanishes and quantum cascade lasers are not efficient enough. Powerful infrared LEDs in this range are needed for applications such as active imaging, organic molecule sensing and airfield lighting. Here we report the design of a HgTe nanocrystal-based LED with luminescence between 2 and 2.3 µm. With an external quantum efficiency of 0.3% and radiance up to 3 W Sr−1 m−2, these HgTe LEDs already present a competitive performance for emission above 2 µm.
Complete list of metadata

https://hal.archives-ouvertes.fr/hal-03478275
Contributor : Emmanuel Lhuillier Connect in order to contact the contributor
Submitted on : Monday, December 13, 2021 - 9:45:23 PM
Last modification on : Wednesday, May 11, 2022 - 3:22:05 PM
Long-term archiving on: : Monday, March 14, 2022 - 7:45:53 PM

File

 Restricted access
To satisfy the distribution rights of the publisher, the document is embargoed until : 2022-06-13

Please log in to resquest access to the document

Identifiers

Citation

Junling Qu, Mateusz Weis, Eva Izquierdo, Simon Gwénaël Mizrahi, Audrey Chu, et al.. Electroluminescence from Nanocrystals above 2 µm. Nature Photonics, Nature Publishing Group, 2022, 16 (1), pp.38-44. ⟨10.1038/s41566-021-00902-y⟩. ⟨hal-03478275⟩

Share

Metrics

Record views

92